Effect of superoxidized water and sodium hypochlorite, associated or not with EDTA, on organic and inorganic components of bovine root dentin.

INTRODUCTION: This study aimed to evaluate the effects of Sterilox (Sx), a superoxidized water, 5% and 2% sodium hypochlorite (5NaOCl and 2NaOCl), and 17% EDTA (E) on the organic and inorganic components of bovine dentin. METHODS: Eighty bovine incisors were randomly divided into 8 groups (n = 10): 5NaOCl, 5NaOCl + E, 2NaOCl, 2NaOCl + E, Sx, Sx + E, E alone, and distilled water (H2O). Root canal instrumentation was performed by using the corresponding irrigant. The apical 15 mm was longitudinally sectioned into 2 fragments, one for light microscopy analysis in slides stained with picrosirius red (organic component) and the other for scanning electron microscopy analysis (inorganic component). Scores data obtained in the light microscopy analysis were submitted to the Kruskal-Wallis test, followed by multiple comparisons test (P < .05). Scanning electron microscopy images were analyzed descriptively. RESULTS: The chemical solution 5NaOCl had a greater effect on the organic component of dentin in area and depth than 2NaOCl. The chemical solutions 5NaOCl + E, 5NaOCl and 2NaOCl + E caused the greatest change in the collagenous organic matrix near the root canal lumen. The chemical solution 2NaOCl showed similar behavior to Sx, associated or not with E, promoting more superficial disorganization of collagen in a smaller area. Demineralization was observed in all groups in which E was used. However, areas of erosion and open dentinal tubules were detected only when it was combined with NaOCl. CONCLUSIONS: Five percent NaOCl promoted the most extensive damage to the organic component of dentin, and when associated to EDTA, dentinal erosion could be seen. Considering these specific aspects, 2% NaOCl and Sx had milder effects on bovine root dentin.

Effect of super-oxidized water, sodium hypochlorite and EDTA on dentin microhardness.

The present study aimed to evaluate the influence of the following irrigating solutions on the microhardness of root canal dentin: 2% sodium hypochlorite (2NaOCl), 5% sodium hypochlorite (5NaOCl), super-oxidized water (400 ppm Sterilox - Sx) and 17% EDTA (E). Eighty roots from bovine incisors were randomly divided into 8 groups (n=10): 2NaOCl, 5NaOCl, Sx, and 2NaOCl + E, 5NaOCl + E, Sx + E (associated with E as final irrigant for 5 min), E solely and distilled water (dH2O) as the negative control. Root canal preparation was performed by hand instruments, using one of the irrigation protocols for 30 min. Then, 5 mm of the cervical root third were cut out from each sample and subjected to the Vickers microhardness test, at two points, one at approximately 500-1000 µm from the root canal lumen (distance 1), and the other at approximately 500-1000 µm from the external root surface (distance 2). Data were analyzed by Wilcoxon and Kruskal-Wallis tests at 5% significance level. Microhardness values at distance 1 were significantly lower than those at distance 2 for all groups, except 5NaOCl and 5NaOCl + E groups (p>0.05). EDTA showed the lowest microhardness values. However, no statistically significant difference was detected among groups at distance 1 and EDTA was significantly different only from Sx at distance 2. In conclusion, all tested solutions showed lower microhardness at the most superficial root canal dentin layer compared to the one found near the external root surface, except 5NaOCl and 5NaOCl + E; EDTA promoted lower microhardness values in comparison to Sterilox at this site.

Effect of Super-Oxidized Water, Sodium Hypochlorite and EDTA on Dentin Microhardness

The present study aimed to evaluate the influence of the following irrigating solutions on the microhardness of root canal dentin: 2% sodium hypochlorite (2NaOCl), 5% sodium hypochlorite (5NaOCl), super-oxidized water (400 ppm Sterilox - Sx) and 17% EDTA (E). Eighty roots from bovine incisors were randomly divided into 8 groups (n=10): 2NaOCl, 5NaOCl, Sx, and 2NaOCl + E, 5NaOCl + E, Sx + E (associated with E as final irrigant for 5 min), E solely and distilled water (dH2O) as the negative control. Root canal preparation was performed by hand instruments, using one of the irrigation protocols for 30 min. Then, 5 mm of the cervical root third were cut out from each sample and subjected to the Vickers microhardness test, at two points, one at approximately 500-1000 µm from the root canal lumen (distance 1), and the other at approximately 500-1000 µm from the external root surface (distance 2). Data were analyzed by Wilcoxon and Kruskal-Wallis tests at 5% significance level. Microhardness values at distance 1 were significantly lower than those at distance 2 for all groups, except 5NaOCl and 5NaOCl + E groups (p>0.05). EDTA showed the lowest microhardness values. However, no statistically significant difference was detected among groups at distance 1 and EDTA was significantly different only from Sx at distance 2. In conclusion, all tested solutions showed lower microhardness at the most superficial root canal dentin layer compared to the one found near the external root surface, except 5NaOCl and 5NaOCl + E; EDTA promoted lower microhardness values in comparison to Sterilox at this site.

O presente estudo teve como objetivo avaliar a influência das seguintes soluções irrigadoras na microdureza da dentina do canal radicular: hipoclorito de sódio a 2% (NaOCl2), hipoclorito de sódio a 5% (NaOCl5), água superoxidada (Sterilox(r) 400 ppm - Sx) e EDTA a 17% (E). Oitenta raízes de incisivos bovinos foram divididas aleatoriamente em 8 grupos (n=10): NaOCl2, NaOCl5, Sx e NaOCl2 + E, NaOCl5 + E, Sx + E (associados ao E como irrigante final por 5 min), E isolado e água destilada (H2Od), como controle negativo. O preparo dos canais radiculares foi realizado com instrumentos manuais, usando um dos protocolos de irrigação por 30 min. A seguir, 5 mm do terço cervical de cada amostra foram cortados perpendicularmente e submetidos ao teste de microdureza de Vickers, em dois pontos, um aproximadamente 500-1000 µm da luz do canal radicular (distância 1), e o outro aproximadamente 500-1000 µm da superfície externa da raiz (distância 2). Os dados foram analisados pelos testes de Wilcoxon e Kruskal-Wallis com um nível de significância de 5%. Os valores de microdureza na distância 1 foram significativamente menores do que na distância 2 para todos os grupos, exceto NaOCl5 e NaOCl5 +E (p>0,05). O EDTA mostrou os menores valores de microdureza. No entanto, não foi detectada diferença estatisticamente significativa entre os grupos na distância 1 e o EDTA foi significativamente diferente apenas do Sx na distância 2. Pode-se concluir que todas as soluções testadas mostraram menor microdureza na camada de dentina mais superficial do canal radicular em comparação aos valores encontrados próximo à superfície radicular externa, exceto NaOCl5 e NaOCl5 + E; o EDTA promoveu menor microdureza em comparação ao Sterilox(r) neste ponto.